Yes, this is good stuff. But won't it lose it's temper anywhere you weld?
<looks around for a HUGE tank of oil to retemper his bike frame welds>
Steel loses it somewhat, but not much. Even less if you braze.
Aluminum will lose a lot though, unless you get the super-low 350F or 500F solder.